Aluminum Industrial Fan Blade For Cooling Towers , Ceiling Aluminum Fan Blades
We are one of the biggest aluminium factory in the east of China . Owning the most species-wide of aluminum profie in the world. Marketing occupancy of Fan blade profile in China is No. 1 .Deep Processing Ability for aluminum and CNC: Fabrication, Drill hole, milling, de-burr, chamfer, stretch bending, welding and so on.
Descrition:
| NO. | ITEM | Aluminum Fan Blade Profile |
| 1 | Material | Aluminum alloy 6000 series |
| 2 | Temper | T4/T5/T6 |
| 3 | Length | Up to 12 meters |
| 4 | Mould | Our standard mould or customized . |
| 5 | Machining | Cutting , Drilling , Bending , Milling etc . |
| 6 | Wall thickness | At least 1 mm |
| 7 | Surface finish | Oxidation,powder coating,etc. |
| 8 | Standard China | GB5237-2008 |
| 9 | Packing way | Shrink Film /Pallet / Wooden Case |
| 10 | Manufacturing process | Aluminum extrusion process |
Specifications:
1. Primary Technical Data
1) Chemical composition
2) Mechanical property
| Alloy | Temper | Tensile strength | Yield strength | Elongation |
| 6063 | T5 | ≥ 160Mpa | ≥ 110Mpa | ≥ 8% |
| T6 | ≥ 205Mpa | ≥ 180Mpa | ≥ 8% |
| 6061 | T6 | ≥ 265Mpa | ≥ 245Mpa | ≥ 8% |
3. Surface Treatment of Sections
|
(Class) | (μm),not diminish than | acid-resistant | abrasion resistance |
| (Min-average film
thickness) | (Min-part film
thickness) | CASS | (S) | |
| (h) | Class | (f, g /μm) |
| AA10 | 10 | 8 | 16 | ≥9 | ≥50 | ≥300 |
| AA15 | 15 | 12 | 32 | ≥9 | ≥75 | ≥300 |
| AA20 | 20 | 16 | 56 | ≥9 | ≥100 | ≥300 |
| AA25 | 25 | 20 | 72 | ≥9 | ≥125 | ≥300 |
Competitive Advantage:
1.High hardness, hard aluminum series.
2.Fair corrosion resistance. Heat treatable
3.Good workability. Good appearance
4.High quality and reasonable price.
5.Our product is your best choice.
Advantages of our company:
1.Owe 600-4000 tons extruders.We could produce big size of profile.
2.Monthly production capacity:4000 tons.
3.99.9% raw aluminum ingot.General ALLOY:6063, 6061,6005, 6060,6082 .
4.We accept small QTY for special alloy.